In microscopy, conductive atomic force microscopy (C-AFM) or current sensing atomic force microscopy (CS-AFM) is a mode in atomic force microscopy (AFM) that simultaneously measures the topography of a material and the electric current flow at the contact point of the tip with the surface of the sample. The topography is measured by detecting the deflection of the cantilever using an optical system (laser + photodiode), while the current is detected using a current-to-voltage preamplifier.[1] The fact that the CAFM uses two different detection systems (optical for the topography and preamplifier for the current) is a strong advantage compared to scanning tunneling microscopy (STM). Basically, in STM the topography picture is constructed based on the current flowing between the tip and the sample (the distance can be calculated depending on the current). Therefore, when a portion of a sample is scanned with an STM, it is not possible to discern if the current fluctuations are related to a change in the topography (due to surface roughness) or to a change in the sample conductivity (due to intrinsic inhomogeneities).

Topographic (left) and current (right) maps collected with CAFM on a polycrystalline HfO2 stack. The images show very good spatial correlation.

The CAFM is usually operated in contact mode; the tip can be kept at one location while the voltage and current signals are applied/read, or it can be moved to scan a specific region of the sample under a constant voltage (and the current is collected). Recently, some manufacturers provide the option of measuring the current in semi-contact mode.[2] The CAFM was first developed by Sean O'Shea and co-workers at the University of Cambridge in 1993,[3] and it is referred to in the literature by several names, including C-AFM, local-conductivity AFM (LC-AFM), conductive probe AFM (CP-AFM), conductive scanning probe microscopy (C-SPM) or conductive scanning force microscopy (C-SFM), although CAFM is the most widespread.

Working principle edit

In order to transform an AFM into a CAFM, three elements are required: i) the probe tip must be conductive, ii) a voltage source is needed to apply a potential difference between the tip and the sample holder, and iii) a preamplifier is used to convert the (analogical) current signal into (digital) voltages that can be read by the computer.[1] In CAFM experiments, the sample is usually fixed on the sample holder using a conductive tape or paste, being silver paints the most widespread.[4] A Faraday cage is also convenient to isolate the sample from any external electrical interference. Using this setup, when a potential difference is imposed between tip and sample an electrical field is generated, which results in a net current flowing from tip-to-sample or vice versa. The currents collected by the CAFM obey the relationship:

 

where I is the total current flowing through the tip/sample nanojunction, J is the current density and Aeff is the effective emission area through which electrons can flow (from now on we will refer to it just as effective area).[1] The most common mistake in CAFM research is to assume that the effective emission area (Aeff) equals the physical contact area (Ac). Strictly, this assumption is erroneous because in many different tip/sample systems the electrical field applied may propagate laterally. For example, when the CAFM tip is placed on a metal the lateral conductivity of the sample is very high, making (in principle) the whole sample surface area electrically connected (Aeff equals the area covered by the metallic film/electrode).[5][6] Aeff has been defined as:"the sum of all those infinitesimal spatial locations on the surface of the sample that are electrically connected to the CAFM tip (the potential difference is negligible). As such, Aeff is a virtual entity that summarizes all electrically relevant effects within the tip/sample contact system into a single value, over which the current density is assumed to be constant."[1] Therefore, when the CAFM tip is placed in contact with a metal (a metallic sample or just a metallic pad on an insulator), the lateral conductivity of the metal is very high, and the CAFM tip can be understood as a current collector (nanosized probe station);[1][5][6] on the contrary, if the CAFM tip is placed directly on an insulator, it acts as a nanosized electrode and provides a very high lateral resolution. The value of Aeff when a Pt-Ir coated tip (with a typical radius of 20 nm) is placed on a SiO2 insulating film has been calculated to be typically 50 nm2.[7][8][9][10][11][12][13] The value of Aeff can fluctuate depending on the environmental conditions, and it can range from 1 nm2 in ultra high vacuum (UHV) to 300 nm2 in very humid environments.[14][15][16] On well-defined single crystal surfaces under UHV conditions it has even been demonstrated that measurements of the local conductivity with atomic resolution are possible.[17]

Applications edit

 
Visualization of conductive filaments in HfO2 thin films for RRAM memories via CAFM.

CAFM was initially used in the field of nanoelectronics to monitor the electrical properties of thin dielectrics with very high lateral resolution. The first CAFM development in 1993 had the goal of studying the local tunneling currents through 12 nm thick SiO2 films.[3] In 1995 and 1996, O'Shea[18] and Ruskell[19] further improved the lateral resolution of the CAFM technique, achieving values of 10 nm and 8 nm, respectively. This enhanced resolution allowed to observe the first topographic-current correlations, and the inhomogeneity observed in the current maps was associated to the presence of local native defects in the oxide. Following works by Olbrich[20][21][22] and Ebersberger[23] reported that, in SiO2 films thinner than 5 nm, the tunneling current increases exponentially with thickness reductions. Consequently, thickness fluctuations of tenths of nanometer in the SiO2 film could create electrically weak spots that reduce the reliability of the whole dielectric film, as the dielectric breakdown (BD) is a stochastic process. The capability of the CAFM for determining the thickness of thin oxides was further demonstrated by Frammelsberger and co-workers[7][24] who statistically analyzed more than 7200 I-V curves, and reported SiO2 thicknesses with a sensitivity of ±0.3 nm. Other local phenomena like charge trapping,[25] trap assisted tunneling[26][27][28][29][30][31] and stress induced leakage current (SILC)[32] can be also easily monitored with CAFM. In general, the CAFM can monitor the effect of any process that introduces local changes in the structure of the dielectric, including thermal annealing,[33][34][12][35][36][16][37] dopping[38] and irradiation,[39][40][41] among others.

 
Number of publications and citations referring to CAFM per year up to June 14th of 2016 (source Web of Science)

Apart from monitoring the electrical properties of a dielectric, the CAFM can be also used to alter its properties by applying an electrical field locally. In particular, the CAFM is especially useful to determine which locations of the samples lead to premature BD, which can provide essential information about the reliability of the samples. The CAFM also helped to confirm the percolation theory of the BD by experimentally proving that this is a very local phenomenon that occurs in small areas typically below 100 nm2.[32] Lateral propagations of the BD event can also be detected by CAFM.[15][42][43] The severity of the BD event can also be studied from the dielectric breakdown induced epitaxy,[26][44][45][46] which can be observed from subsequent topographic images collected with the CAFM after the voltage ramp. Similarly, the analysis of the BD recovery (resistive switching, RS) can also be monitored by CAFM.[47][48][49][50] All the capabilities of the CAFM for studying resistive switching in dielectrics have been summarized in the review article of reference.[51] Unlike a normal AFM, the CAFM can be also used to perform local photolithography via bias-assisted local anodic oxidation (LAO). Nowadays the CAFM technique has expanded to many other fields of science, including physics, materials science, chemistry and engineering (among many others), and it has been used to study different materials and/or structures, including nanoparticles,[52][53] molecules,[54] nanowires,[55] carbon nanotubes,[56] two dimensional (2D) materials,[57][58][59][60][61] coatings,[62][63][64] photoelectricity[65] and piezoelectricity[66] (among others). As of June 14 of 2016, the CAFM had been used in 1325 journal research articles, and it has become a popular tool in nanosciences.[1]

CAFM probes edit

 
(Left) Standard metal-varnished nanoprobe for CAFM. (Right) Standard metal-varnished nanoprobe for CAFM coated with a thin film of single layer graphene. (Center) Schematic of the graphene coated nanoprobe.

The main problem of the CAFM is that the probes are more expensive and wear out faster than those used in topographic AFM maps, mainly due to the high current densities flowing through the tip/sample nanojunction, but also due to lateral friction. The premature degradation of a CAFM tip not only increases the cost of the experiments, but also reduces the reliability of the data collected. For this reason, when using CAFM, tip conductivity characterization (using a reference sample) before and after the experiments is highly recommended; only if the CAFM tip holds the same conductivity before and after is the data collected considered reliable. The first types of conductive nanoprobes used in CAFM experiments, which are still widely used nowadays, consist on standard silicon nanoprobes (as those used in topographic AFM measurements) varnished with thin metallic films, including Pt, Au, Ru, Ti and Cr, among others.[3][7][67] The varnish should be thick enough to withstand the large current densities and frictions, and at the same time thin enough to not increase significantly the radius of the tip apex, maintaining its sharpness and ensuring a high lateral resolution of the CAFM technique. As mentioned, the lifetime of the metal-varnished tips for CAFM experiments is much shorter than in any other AFM mode, mainly due to metallic varnish melting and loss of tip mass during the scans. To solve this problem, CAFM silicon tips varnished with hard materials like phosphorus-doped diamond have appeared.[67] The main problems of diamond-coapted CAFM tips are: i) they are much more expensive, and ii) they are very stiff and can damage (scratch) the surface of the samples under tests. Another option is to use sharpened metallic wires as the tip, but also the use of hone techniques increases their price (compared to metal-coated Si tips). Furthermore, these tips can also degrade (lose their conductivity) by particle adhesion. A cheap and effective methodology to protect CAFM tips from degrading is to coat them with graphene, which can withstand well the high current densities and mechanical friction. Moreover, graphene is inert and slows down particle adhesion to the tip apex.

The preamplifier edit

 
Schematic of a basic current-to-voltage preamplifier for CAFM.

The analogical current signals flowing through the tip/sample nanojunction are sent to the preamplifier, which transforms them into digital voltages that can be read by the data acquisition (DAQ) card of the computer. Many manufacturers integrate the preamplifier in the so-called "CAFM application module", which is a removable component that can be fixed to the AFM (usually very near to the tip to minimize the electrical noise) to perform conductivity measurements. Similarly, many other modules allow AFMs to perform other operations, like scanning capacitance microscopy (SCM) or scanning spreading resistance microscopy (SSRM). In most CAFM experiments the currents measured typically can range between a few picoamperes and hundreds of microamperes, while the voltages readable by the DAQ card usually range between -3 V to +3V.[68] Therefore, the preamplifier needs to provide a very low noise and a high transimpedance (gain). Figure 2 shows the simplified schematic of a typical low noise preamplifier for CAFM measurements,[69] in which some elements can be distinguished: i) an operational amplifier with high input impedance; ii) a feedback resistor (Rf) and its parasite capacitor (Cs) and Johnson noise (et) associated effects; iii) a noise voltage source associated to the operational amplifier (en); and iv) a capacitance associated to the input interconnections (Ci). A correct selection of the electrical components is essential to achieve good and reliable CAFM data acquisition. For example, the value of Rf is not trivial: a very high value of Rf improves the noise-signal ratio, while reduces the bandwidth of the preamplifier. Therefore, the value of Rf should be chosen to provide enough bandwidth and a noise level below the current values that we want to measure. The parameter en can be easily reduced by using a commercial low noise operational amplifier. The capacitance associated to the connections (Ci) can be easily minimized by placing the preamplifier as near as possible to the conductive tip. The company FEMTO, one of the world leading manufacturers of preamplifiers compatible with CAFMs, can provide devices with electrical noise as low as 3 fA and a gain up to 1013 V/A.[70] Nevertheless, the main limitation of CAFM preamplifiers is their narrow current dynamic range, which usually allows collecting electrical signals only within three or four orders of magnitude (or even less). To solve this problem preamplifiers with an adjustable gain can be used to focus on specific ranges.[70] A more sophisticated solution for this problem is to combine the CAFM with a sourcemeter,[71][72] semiconductor parameter analyzer or with a logarithmic preamplifier,[73] which can capture the currents flowing through the tip/sample system at any range and with a high resolution.

References edit

  1. ^ a b c d e f Lanza, Mario (2017). Conductive Atomic Force Microscopy. Berlin, Germany: Wiley-VCH. p. 400. ISBN 978-3-527-34091-0.
  2. ^ "PeakForce TUNA - Bruker AFM Probes". www.brukerafmprobes.com. Retrieved 2017-02-04.
  3. ^ a b c Murrell, M. P.; Welland, M. E.; O'Shea, S. J.; Wong, T. M. H.; Barnes, J. R.; McKinnon, A. W.; Heyns, M.; Verhaverbeke, S. (1993-02-15). "Spatially resolved electrical measurements of SiO2 gate oxides using atomic force microscopy". Applied Physics Letters. 62 (7): 786–788. Bibcode:1993ApPhL..62..786M. doi:10.1063/1.108579. ISSN 0003-6951.
  4. ^ "Silver Paints/Pastes : SPI Supplies". www.2spi.com. Retrieved 2017-02-04.
  5. ^ a b Rommel, Mathias; Jambreck, Joachim D.; Lemberger, Martin; Bauer, Anton J.; Frey, Lothar; Murakami, Katsuhisa; Richter, Christoph; Weinzierl, Philipp (2012-11-29). "Influence of parasitic capacitances on conductive AFM I-V measurements and approaches for its reduction". Journal of Vacuum Science & Technology B, Nanotechnology and Microelectronics: Materials, Processing, Measurement, and Phenomena. 31 (1): 01A108. Bibcode:2013JVSTB..31aA108R. doi:10.1116/1.4768679. ISSN 2166-2746.
  6. ^ a b Yanev, V.; Erlbacher, T.; Rommel, M.; Bauer, A.J.; Frey, L. (July 2009). "Comparative study between conventional macroscopic IV techniques and advanced AFM based methods for electrical characterization of dielectrics at the nanoscale". Microelectronic Engineering. 86 (7–9): 1911–1914. doi:10.1016/j.mee.2009.03.094.
  7. ^ a b c Frammelsberger, Werner; Benstetter, Guenther; Kiely, Janice; Stamp, Richard (2007-01-30). "C-AFM-based thickness determination of thin and ultra-thin SiO2 films by use of different conductive-coated probe tips". Applied Surface Science. 253 (7): 3615–3626. Bibcode:2007ApSS..253.3615F. doi:10.1016/j.apsusc.2006.07.070.
  8. ^ Zhang, Kai; Lanza, Mario; Shen, Ziyong; Fu, Qiang; Hou, Shimin; Porti, Marc; Nafría, Montserrat (2014-05-04). "Analysis of Factors in the Nanoscale Physical and Electrical Characterization of High-K Materials by Conductive Atomic Force Microscope". Integrated Ferroelectrics. 153 (1): 1–8. Bibcode:2014InFer.153....1Z. doi:10.1080/10584587.2014.902280. ISSN 1058-4587. S2CID 94116742.
  9. ^ Pirrotta, Onofrio; Larcher, Luca; Lanza, Mario; Padovani, Andrea; Porti, Marc; Nafría, Montserrat; Bersuker, Gennadi (2013-10-01). "Leakage current through the poly-crystalline HfO2: Trap densities at grains and grain boundaries". Journal of Applied Physics. 114 (13): 134503–134503–5. Bibcode:2013JAP...114m4503P. doi:10.1063/1.4823854. ISSN 0021-8979.
  10. ^ Lanza, M.; Porti, M.; Nafria, M.; Aymerich, X.; Sebastiani, A.; Ghidini, G.; Vedda, A.; Fasoli, M. (2009-12-01). "Combined Nanoscale and Device-Level Degradation Analysis of Layers of MOS Nonvolatile Memory Devices". IEEE Transactions on Device and Materials Reliability. 9 (4): 529–536. doi:10.1109/TDMR.2009.2027228. ISSN 1530-4388. S2CID 28464435.
  11. ^ Lanza, M.; Porti, M.; Nafría, M.; Aymerich, X.; Ghidini, G.; Sebastiani, A. (September 2009). "Trapped charge and stress induced leakage current (SILC) in tunnel SiO2 layers of de-processed MOS non-volatile memory devices observed at the nanoscale". Microelectronics Reliability. 49 (9–11): 1188–1191. doi:10.1016/j.microrel.2009.06.016.
  12. ^ a b Lanza, M.; Porti, M.; Nafria, M.; Aymerich, X.; Benstetter, G.; Lodermeier, E.; Ranzinger, H.; Jaschke, G.; Teichert, S.; Wilde, L.; Michalowski, P. (July 2009). "Crystallization and silicon diffusion nanoscale effects on the electrical properties of Al2O3 based devices". Microelectronic Engineering. 86 (7–9): 1921–1924. doi:10.1016/j.mee.2009.03.020.
  13. ^ Lanza, M.; Porti, M.; Nafria, M.; Benstetter, G.; Frammelsberger, W.; Ranzinger, H.; Lodermeier, E.; Jaschke, G. (September 2007). "Influence of the manufacturing process on the electrical properties of thin (<4 nm) Hafnium based high-k stacks observed with CAFM". Microelectronics Reliability. 47 (9–11): 1424–1428. doi:10.1016/j.microrel.2007.07.045.
  14. ^ Lanza, M.; Porti, M.; Nafría, M.; Aymerich, X.; Whittaker, E.; Hamilton, B. (2010-10-01). "Note: Electrical resolution during conductive atomic force microscopy measurements under different environmental conditions and contact forces". Review of Scientific Instruments. 81 (10): 106110–106110–3. Bibcode:2010RScI...81j6110L. doi:10.1063/1.3491956. ISSN 0034-6748. PMID 21034138.
  15. ^ a b Lanza, M.; Porti, M.; Nafría, M.; Aymerich, X.; Whittaker, E.; Hamilton, B. (September 2010). "UHV CAFM characterization of high-k dielectrics: Effect of the technique resolution on the pre- and post-breakdown electrical measurements". Microelectronics Reliability. 50 (9–11): 1312–1315. doi:10.1016/j.microrel.2010.07.049.
  16. ^ a b Lanza, Mario; Iglesias, Vanessa; Porti, Marc; Nafria, Montse; Aymerich, Xavier (2011-01-31). "Polycrystallization effects on the nanoscale electrical properties of high-k dielectrics". Nanoscale Research Letters. 6 (1): 108. Bibcode:2011NRL.....6..108L. doi:10.1186/1556-276x-6-108. ISSN 1556-276X. PMC 3211152. PMID 21711617.
  17. ^ Rodenbücher, C.; Bihlmayer, G.; Speier, W.; Kubacki, J.; Wojtyniak, M.; Rogala, M.; Wrana, D.; Krok, F.; Szot, K. (2018). "Local surface conductivity of transition metal oxides mapped with true atomic resolution". Nanoscale. 10 (24): 11498–11505. arXiv:1611.07773. doi:10.1039/C8NR02562B. PMID 29888770. S2CID 47013247.
  18. ^ O'Shea, S. J.; Atta, R. M.; Murrell, M. P.; Welland, M. E. (1995-09-01). "Conducting atomic force microscopy study of silicon dioxide breakdown". Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures Processing, Measurement, and Phenomena. 13 (5): 1945–1952. Bibcode:1995JVSTB..13.1945O. doi:10.1116/1.588113. ISSN 1071-1023.
  19. ^ Ruskell, Todd G.; Workman, Richard K.; Chen, Dong; Sarid, Dror; Dahl, Sarah; Gilbert, Stephen (1996-01-01). "High resolution Fowler-Nordheim field emission maps of thin silicon oxide layers". Applied Physics Letters. 68 (1): 93–95. Bibcode:1996ApPhL..68...93R. doi:10.1063/1.116782. ISSN 0003-6951.
  20. ^ Olbrich, A.; Ebersberger, B.; Boit, C. (1998-03-01). "Nanoscale electrical characterization of thin oxides with conducting atomic force microscopy". 1998 IEEE International Reliability Physics Symposium Proceedings 36th Annual (Cat No 98CH36173) RELPHY-98. pp. 163–168. doi:10.1109/RELPHY.1998.670490. ISBN 978-0-7803-4400-6. S2CID 110367701.
  21. ^ Olbrich, Alexander; Ebersberger, Bernd; Boit, Christian (1998-11-19). "Conducting atomic force microscopy for nanoscale electrical characterization of thin SiO2". Applied Physics Letters. 73 (21): 3114–3116. Bibcode:1998ApPhL..73.3114O. doi:10.1063/1.122690. ISSN 0003-6951.
  22. ^ Olbrich, Alexander; Ebersberger, Bernd; Boit, Christian; Vancea, J.; Hoffmarm, H. (June 1999). "A new AFM-based tool for testing dielectric quality and reliability on a nanometer scale". Microelectronics Reliability. 39 (6–7): 941–946. doi:10.1016/S0026-2714(99)00127-4.
  23. ^ Ebersberger, B.; Boit, C.; Benzinger, H.; Gunther, E. (1996-04-01). "Thickness mapping of thin dielectrics with emission microscopy and conductive atomic force microscopy for assessment of dielectrics reliability". Proceedings of International Reliability Physics Symposium RELPHY-96. pp. 126–130. doi:10.1109/RELPHY.1996.492072. ISBN 978-0-7803-2753-5. S2CID 109344701.
  24. ^ Frammelsberger, Werner; Benstetter, Guenther; Kiely, Janice; Stamp, Richard (2006). "Thickness determination of thin and ultra-thin SiO2 films by C-AFM IV-spectroscopy". Applied Surface Science. 252 (6): 2375–2388. Bibcode:2006ApSS..252.2375F. doi:10.1016/j.apsusc.2005.04.010.
  25. ^ Polspoel, W.; Vandervorst, W. (March 2007). "Evaluation of trap creation and charging in thin SiO2 using both SCM and C-AFM". Microelectronic Engineering. 84 (3): 495–500. doi:10.1016/j.mee.2006.10.074.
  26. ^ a b Nasyrov, K. A.; Shaimeev, S. S.; Gritsenko, V. A. (2009-12-24). "Trap-assisted tunneling hole injection in SiO2: Experiment and theory". Journal of Experimental and Theoretical Physics. 109 (5): 786. Bibcode:2009JETP..109..786N. doi:10.1134/S1063776109110089. ISSN 1063-7761. S2CID 122592036.
  27. ^ Fiorenza, Patrick; Polspoel, Wouter; Vandervorst, Wilfried (2006-05-29). "Conductive atomic force microscopy studies of thin SiO2 layer degradation". Applied Physics Letters. 88 (22): 222104. Bibcode:2006ApPhL..88v2104F. doi:10.1063/1.2208370. ISSN 0003-6951.
  28. ^ Wu, You-Lin; Lin, Shi-Tin (2006-03-01). "Two-trap-assisted tunneling model for post-breakdown I-V characteristics in ultrathin silicon dioxide". IEEE Transactions on Device and Materials Reliability. 6 (1): 75–80. doi:10.1109/TDMR.2006.870351. ISSN 1530-4388.
  29. ^ Pakes, C. I.; Ramelow, S.; Prawer, S.; Jamieson, D. N. (2004-04-13). "Nanoscale electrical characterization of trap-assisted quasibreakdown fluctuations in SiO2". Applied Physics Letters. 84 (16): 3142–3144. Bibcode:2004ApPhL..84.3142P. doi:10.1063/1.1712033. ISSN 0003-6951.
  30. ^ Degraeve, R.; Kaczer, B.; Schuler, F.; Lorenzini, M.; Wellekens, D.; Hendrickx, P.; Houdt, J. Van; Haspeslagh, L.; Tempel, G. (2001-12-01). "Statistical model for stress-induced leakage current and pre-breakdown current jumps in ultra-thin oxide layers". International Electron Devices Meeting. Technical Digest (Cat. No.01CH37224). pp. 6.2.1–6.2.4. doi:10.1109/IEDM.2001.979447. ISBN 978-0-7803-7050-0. S2CID 27991853.
  31. ^ Porti, M.; Nafría, M.; Aymerich, X.; Olbrich, A.; Ebersberger, B. (2002-01-29). "Electrical characterization of stressed and broken down SiO2 films at a nanometer scale using a conductive atomic force microscope". Journal of Applied Physics. 91 (4): 2071–2079. Bibcode:2002JAP....91.2071P. doi:10.1063/1.1430542. ISSN 0021-8979.
  32. ^ a b Tan, Tingting; Liu, Zhengtang; Tian, Hao; Liu, Wenting (2010-07-25). "Low voltage stress-induced leakage current in HfO2 dielectric films". Materials Science and Engineering: B. 171 (1–3): 159–161. doi:10.1016/j.mseb.2010.03.091.
  33. ^ Ang, D. S.; Ong, Y. C.; O'Shea, S. J.; Pey, K. L.; Tung, C. H.; Kawanago, T.; Kakushima, K.; Iwai, H. (2008-05-12). "Polarity dependent breakdown of the high-κ/SiOx gate stack: A phenomenological explanation by scanning tunneling microscopy". Applied Physics Letters. 92 (19): 192904. Bibcode:2008ApPhL..92s2904A. doi:10.1063/1.2926655. ISSN 0003-6951.
  34. ^ Lu, X. B.; Zhang, X.; Huang, R.; Lu, H. B.; Chen, Z. H.; Zhou, H. W.; Wang, X. P.; Nguyen, B. Y.; Wang, C. Z. (2004-10-01). "Effect of post-annealing on the physical and electrical properties of LaAlO/Sub 3/ Gate dielectrics". Proceedings. 7th International Conference on Solid-State and Integrated Circuits Technology, 2004. Vol. 1. pp. 419–422 vol.1. doi:10.1109/ICSICT.2004.1435039. ISBN 978-0-7803-8511-5. S2CID 25239456.
  35. ^ Lanza, M.; Porti, M.; Nafría, M.; Aymerich, X.; Benstetter, G.; Lodermeier, E.; Ranzinger, H.; Jaschke, G.; Teichert, S. (2011-03-01). "Conductivity and Charge Trapping After Electrical Stress in Amorphous and Polycrystalline Devices Studied With AFM-Related Techniques". IEEE Transactions on Nanotechnology. 10 (2): 344–351. Bibcode:2011ITNan..10..344L. doi:10.1109/TNANO.2010.2041935. ISSN 1536-125X. S2CID 28810246.
  36. ^ Bayerl, A.; Lanza, M.; Porti, M.; Nafria, M.; Aymerich, X.; Campabadal, F.; Benstetter, G. (2011-09-01). "Nanoscale and Device Level Gate Conduction Variability of High-k Dielectrics-Based Metal-Oxide-Semiconductor Structures". IEEE Transactions on Device and Materials Reliability. 11 (3): 495–501. doi:10.1109/TDMR.2011.2161087. ISSN 1530-4388. S2CID 22874323.
  37. ^ Bayerl, Albin; Lanza, Mario; Aguilera, Lidia; Porti, Marc; Nafría, Montserrat; Aymerich, Xavier; Gendt, Stefan de (June 2013). "Nanoscale and device level electrical behavior of annealed ALD Hf-based gate oxide stacks grown with different precursors". Microelectronics Reliability. 53 (6): 867–871. doi:10.1016/j.microrel.2013.02.005.
  38. ^ Muenstermann, Ruth; Menke, Tobias; Dittmann, Regina; Mi, Shaobo; Jia, Chun-Lin; Park, Daesung; Mayer, Joachim (2010-12-15). "Correlation between growth kinetics and nanoscale resistive switching properties of SrTiO3 thin films". Journal of Applied Physics. 108 (12): 124504–124504–8. Bibcode:2010JAP...108l4504M. doi:10.1063/1.3520674. ISSN 0021-8979.
  39. ^ Wu, Y. L.; Lin, S. T.; Chang, T. M.; Liou, J. J. (2007-06-01). "Nanoscale Bias-Annealing Effect in Postirradiated Thin Silicon Dioxide Films Observed by Conductive Atomic Force Microscopy". IEEE Transactions on Device and Materials Reliability. 7 (2): 351–355. doi:10.1109/TDMR.2007.901069. ISSN 1530-4388. S2CID 23406644.
  40. ^ Wu, You-Lin; Lin, Shi-Tin; Chang, Tsung-Min; Liou, Juin J. (February 2007). "Reliability study of ultrathin oxide films subject to irradiation-then-stress treatment using conductive atomic force microscopy". Microelectronics Reliability. 47 (2–3): 419–421. doi:10.1016/j.microrel.2006.05.014.
  41. ^ Porti, M.; Nafria, N.; Gerardin, S.; Aymerich, X.; Cester, A.; Paccagnella, A.; Ghidini, G. (2009-01-01). "Implanted and irradiated SiO2/Si structure electrical properties at the nanoscale". Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures Processing, Measurement, and Phenomena. 27 (1): 421–425. Bibcode:2009JVSTB..27..421P. doi:10.1116/1.3043475. ISSN 1071-1023.
  42. ^ Blasco, X.; Nafría, M.; Aymerich, X.; Vandervorst, W. (2005). "Comparison of SiO2 and HfO2/SiO2 gate stacks electrical behaviour at a nanometre scale with CAFM". Electronics Letters. 41 (12): 719. Bibcode:2005ElL....41..719B. doi:10.1049/el:20050805.
  43. ^ Wu, You-Lin; Lin, Shi-Tin (February 2008). "Breakdown spots propagation in ultra-thin SiO2 films under repetitive ramped voltage stress using conductive atomic force microscopy". Journal of Physics and Chemistry of Solids. 69 (2–3): 470–474. Bibcode:2008JPCS...69..470W. doi:10.1016/j.jpcs.2007.07.077.
  44. ^ Tung, C. H.; Pey, K. L.; Lin, W. H.; Radhakrishnan, M. K. (2002-09-01). "Polarity-dependent dielectric breakdown-induced epitaxy (DBIE) in Si MOSFETs". IEEE Electron Device Letters. 23 (9): 526–528. Bibcode:2002IEDL...23..526T. doi:10.1109/LED.2002.802662. ISSN 0741-3106.
  45. ^ Polspoel, W.; Favia, P.; Mody, J.; Bender, H.; Vandervorst, W. (2009-07-15). "Physical degradation of gate dielectrics induced by local electrical stress using conductive atomic force microscopy". Journal of Applied Physics. 106 (2): 024101–024101–7. Bibcode:2009JAP...106b4101P. doi:10.1063/1.3153965. ISSN 0021-8979.
  46. ^ Porti, M.; Nafría, M.; Blüm, M. C.; Aymerich, X.; Sadewasser, S. (2003-06-10). "Atomic force microscope topographical artifacts after the dielectric breakdown of ultrathin SiO2 films". Surface Science. 532–535: 727–731. Bibcode:2003SurSc.532..727P. doi:10.1016/S0039-6028(03)00150-X.
  47. ^ Lanza, M.; Bersuker, G.; Porti, M.; Miranda, E.; Nafría, M.; Aymerich, X. (2012-11-05). "Resistive switching in hafnium dioxide layers: Local phenomenon at grain boundaries". Applied Physics Letters. 101 (19): 193502. Bibcode:2012ApPhL.101s3502L. doi:10.1063/1.4765342. ISSN 0003-6951.
  48. ^ Lanza, M.; Zhang, K.; Porti, M.; Nafría, M.; Shen, Z. Y.; Liu, L. F.; Kang, J. F.; Gilmer, D.; Bersuker, G. (2012-03-19). "Grain boundaries as preferential sites for resistive switching in the HfO2 resistive random access memory structures". Applied Physics Letters. 100 (12): 123508. Bibcode:2012ApPhL.100l3508L. doi:10.1063/1.3697648. ISSN 0003-6951.
  49. ^ Shi, Yuanyuan; Ji, Yanfeng; Hui, Fei; Nafria, Montserrat; Porti, Marc; Bersuker, Gennadi; Lanza, Mario (2015-04-01). "In Situ Demonstration of the Link Between Mechanical Strength and Resistive Switching in Resistive Random-Access Memories". Advanced Electronic Materials. 1 (4): n/a. doi:10.1002/aelm.201400058. ISSN 2199-160X. S2CID 110305072.
  50. ^ Shi, Yuanyuan; Ji, Yanfeng; Hui, Fei; Iglesias, Vanessa; Porti, Marc; Nafria, Montserrat; Miranda, Enrique; Bersuker, Gennadi; Lanza, Mario (2014-08-08). "(Invited) Elucidating the Origin of Resistive Switching in Ultrathin Hafnium Oxides through High Spatial Resolution Tools". ECS Transactions. 64 (14): 19–28. Bibcode:2014ECSTr..64n..19S. doi:10.1149/06414.0019ecst. ISSN 1938-6737.
  51. ^ Lanza, Mario (2014-03-13). "A Review on Resistive Switching in High-k Dielectrics: A Nanoscale Point of View Using Conductive Atomic Force Microscope". Materials. 7 (3): 2155–2182. Bibcode:2014Mate....7.2155L. doi:10.3390/ma7032155. PMC 5453275. PMID 28788561.
  52. ^ Sze, J. Y.; Tay, B. K.; Pakes, C. I.; Jamieson, D. N.; Prawer, S. (2005-09-15). "Conducting Ni nanoparticles in an ion-modified polymer". Journal of Applied Physics. 98 (6): 066101–066101–3. Bibcode:2005JAP....98f6101S. doi:10.1063/1.2014938. ISSN 0021-8979.
  53. ^ Shi, Yuanyuan; Ji, Yanfeng; Sun, Hui; Hui, Fei; Hu, Jianchen; Wu, Yaxi; Fang, Jianlong; Lin, Hao; Wang, Jianxiang (2015-07-16). "Nanoscale characterization of PM2.5 airborne pollutants reveals high adhesiveness and aggregation capability of soot particles". Scientific Reports. 5: 11232. Bibcode:2015NatSR...511232S. doi:10.1038/srep11232. ISSN 2045-2322. PMC 4503936. PMID 26177695.
  54. ^ Cui, X. D.; Primak, A.; Zarate, X.; Tomfohr, J.; Sankey, O. F.; Moore, A. L.; Moore, T. A.; Gust, D.; Harris, G. (2001-10-19). "Reproducible Measurement of Single-Molecule Conductivity". Science. 294 (5542): 571–574. Bibcode:2001Sci...294..571C. doi:10.1126/science.1064354. ISSN 0036-8075. PMID 11641492. S2CID 26028013.
  55. ^ Wang, Zhong Lin; Song, Jinhui (2006-04-14). "Piezoelectric Nanogenerators Based on Zinc Oxide Nanowire Arrays". Science. 312 (5771): 242–246. Bibcode:2006Sci...312..242W. doi:10.1126/science.1124005. ISSN 0036-8075. PMID 16614215. S2CID 4810693.
  56. ^ Zhou, Chongwu; Kong, Jing; Dai, Hongjie (2000-03-14). "Electrical measurements of individual semiconducting single-walled carbon nanotubes of various diameters". Applied Physics Letters. 76 (12): 1597–1599. Bibcode:2000ApPhL..76.1597Z. doi:10.1063/1.126107. ISSN 0003-6951. S2CID 17973840.
  57. ^ Iglesias, V.; Porti, M.; Nafría, M.; Aymerich, X.; Dudek, P.; Schroeder, T.; Bersuker, G. (2010-12-27). "Correlation between the nanoscale electrical and morphological properties of crystallized hafnium oxide-based metal oxide semiconductor structures". Applied Physics Letters. 97 (26): 262906. Bibcode:2010ApPhL..97z2906I. doi:10.1063/1.3533257. ISSN 0003-6951.
  58. ^ Vecchio, Carmelo; Sonde, Sushant; Bongiorno, Corrado; Rambach, Martin; Yakimova, Rositza; Raineri, Vito; Giannazzo, Filippo (2011-03-29). "Nanoscale structural characterization of epitaxial graphene grown on off-axis 4H-SiC (0001)". Nanoscale Research Letters. 6 (1): 269. Bibcode:2011NRL.....6..269V. doi:10.1186/1556-276x-6-269. ISSN 1556-276X. PMC 3211332. PMID 21711803.
  59. ^ Giannazzo, Filippo; Sonde, Sushant; Rimini, Emanuele; Raineri, Vito (2011-01-31). "Lateral homogeneity of the electronic properties in pristine and ion-irradiated graphene probed by scanning capacitance spectroscopy". Nanoscale Research Letters. 6 (1): 109. Bibcode:2011NRL.....6..109G. doi:10.1186/1556-276x-6-109. ISSN 1556-276X. PMC 3211153. PMID 21711643.
  60. ^ Ji, Yanfeng; Pan, Chengbin; Zhang, Meiyun; Long, Shibing; Lian, Xiaojuan; Miao, Feng; Hui, Fei; Shi, Yuanyuan; Larcher, Luca; Wu, Ernest; Lanza, Mario (2016-01-04). "Boron nitride as two dimensional dielectric: Reliability and dielectric breakdown". Applied Physics Letters. 108 (1): 012905. Bibcode:2016ApPhL.108a2905J. doi:10.1063/1.4939131. ISSN 0003-6951.
  61. ^ Lanza, Mario; Wang, Yan; Gao, Teng; Bayerl, Albin; Porti, Marc; Nafria, Montserrat; Zhou, Yangbo; Jing, Guangyin; Zhang, Yanfeng (2013-05-21). "Electrical and mechanical performance of graphene sheets exposed to oxidative environments". Nano Research. 6 (7): 485–495. doi:10.1007/s12274-013-0326-6. ISSN 1998-0124. S2CID 97263039.
  62. ^ Tan, Susheng; Tang, Zhiyong; Liang, Xiaorong; Kotov, Nicholas A. (2004-09-01). "Resonance Tunneling Diode Structures on CdTe Nanowires Made by Conductive AFM". Nano Letters. 4 (9): 1637–1641. Bibcode:2004NanoL...4.1637T. doi:10.1021/nl0492077. ISSN 1530-6984.
  63. ^ Jiang, Lanlan; Xiao, Na; Wang, Bingru; Grustan-Gutierrez, Enric; Jing, Xu; Babor, Petr; Kolíbal, Miroslav; Lu, Guangyuan; Wu, Tianru (2017-01-26). "High-resolution characterization of hexagonal boron nitride coatings exposed to aqueous and air oxidative environments". Nano Research. 10 (6): 2046–2055. doi:10.1007/s12274-016-1393-2. ISSN 1998-0124. S2CID 99473899.
  64. ^ Shi, Yuanyuan; Ji, Yanfeng; Hui, Fei; Wu, Hai-Hua; Lanza, Mario (2014-09-04). "Ageing mechanisms and reliability of graphene-based electrodes". Nano Research. 7 (12): 1820–1831. doi:10.1007/s12274-014-0542-8. ISSN 1998-0124. S2CID 54516801.
  65. ^ Howell, Sarah L.; Padalkar, Sonal; Yoon, KunHo; Li, Qiming; Koleske, Daniel D.; Wierer, Jonathan J.; Wang, George T.; Lauhon, Lincoln J. (2013-11-13). "Spatial Mapping of Efficiency of GaN/InGaN Nanowire Array Solar Cells Using Scanning Photocurrent Microscopy". Nano Letters. 13 (11): 5123–5128. Bibcode:2013NanoL..13.5123H. doi:10.1021/nl402331u. ISSN 1530-6984. PMID 24099617.
  66. ^ Pan, Chengbin; Hu, Jianchen; Grustan-Gutierrez, Enric; Hoang, Minh Tuan; Duan, Huiling; Yvonnet, Julien; Mitrushchenkov, Alexander; Chambaud, Gilberte; Lanza, Mario (2016-04-21). "Suppression of nanowire clustering in hybrid energy harvesters". J. Mater. Chem. C. 4 (16): 3646–3653. doi:10.1039/c6tc00468g. ISSN 2050-7534.
  67. ^ a b "NanoWorld".
  68. ^ "National Instriuments".
  69. ^ Tiedje, T.; Brown, A. (1990-07-15). "Performance limits for the scanning tunneling microscope". Journal of Applied Physics. 68 (2): 649–654. Bibcode:1990JAP....68..649T. doi:10.1063/1.346794. ISSN 0021-8979.
  70. ^ a b "FEMTO". Retrieved 4 February 2016.
  71. ^ Lanza, M.; Bayerl, A.; Gao, T.; Porti, M.; Nafria, M.; Jing, G. Y.; Zhang, Y. F.; Liu, Z. F.; Duan, H. L. (2013-03-13). "Graphene-Coated Atomic Force Microscope Tips for Reliable Nanoscale Electrical Characterization". Advanced Materials. 25 (10): 1440–1444. Bibcode:2013AdM....25.1440L. doi:10.1002/adma.201204380. ISSN 1521-4095. PMID 23280635. S2CID 205248208.
  72. ^ Hui, Fei; Vajha, Pujashree; Shi, Yuanyuan; Ji, Yanfeng; Duan, Huiling; Padovani, Andrea; Larcher, Luca; Li, Xiao Rong; Lanza, Mario (2016-04-21). "Moving graphene devices from lab to market: advanced graphene-coated nanoprobes". Nanoscale. 8 (16): 8466–8473. Bibcode:2016Nanos...8.8466H. doi:10.1039/c5nr06235g. ISSN 2040-3372. PMID 26593053.
  73. ^ Aguilera, L.; Lanza, M.; Porti, M.; Grifoll, J.; Nafría, M.; Aymerich, X. (2008-07-01). "Improving the electrical performance of a conductive atomic force microscope with a logarithmic current-to-voltage converter". Review of Scientific Instruments. 79 (7): 073701–073701–5. Bibcode:2008RScI...79g3701A. doi:10.1063/1.2952058. ISSN 0034-6748. PMID 18681702.

May 03, 2024
conductive, atomic, force, microscopy, this, article, relies, excessively, references, primary, sources, please, improve, this, article, adding, secondary, tertiary, sources, find, sources, news, newspapers, books, scholar, jstor, november, 2017, learn, when, . This article relies excessively on references to primary sources Please improve this article by adding secondary or tertiary sources Find sources Conductive atomic force microscopy news newspapers books scholar JSTOR November 2017 Learn how and when to remove this message In microscopy conductive atomic force microscopy C AFM or current sensing atomic force microscopy CS AFM is a mode in atomic force microscopy AFM that simultaneously measures the topography of a material and the electric current flow at the contact point of the tip with the surface of the sample The topography is measured by detecting the deflection of the cantilever using an optical system laser photodiode while the current is detected using a current to voltage preamplifier 1 The fact that the CAFM uses two different detection systems optical for the topography and preamplifier for the current is a strong advantage compared to scanning tunneling microscopy STM Basically in STM the topography picture is constructed based on the current flowing between the tip and the sample the distance can be calculated depending on the current Therefore when a portion of a sample is scanned with an STM it is not possible to discern if the current fluctuations are related to a change in the topography due to surface roughness or to a change in the sample conductivity due to intrinsic inhomogeneities Topographic left and current right maps collected with CAFM on a polycrystalline HfO2 stack The images show very good spatial correlation The CAFM is usually operated in contact mode the tip can be kept at one location while the voltage and current signals are applied read or it can be moved to scan a specific region of the sample under a constant voltage and the current is collected Recently some manufacturers provide the option of measuring the current in semi contact mode 2 The CAFM was first developed by Sean O Shea and co workers at the University of Cambridge in 1993 3 and it is referred to in the literature by several names including C AFM local conductivity AFM LC AFM conductive probe AFM CP AFM conductive scanning probe microscopy C SPM or conductive scanning force microscopy C SFM although CAFM is the most widespread Contents 1 Working principle 2 Applications 3 CAFM probes 4 The preamplifier 5 ReferencesWorking principle editIn order to transform an AFM into a CAFM three elements are required i the probe tip must be conductive ii a voltage source is needed to apply a potential difference between the tip and the sample holder and iii a preamplifier is used to convert the analogical current signal into digital voltages that can be read by the computer 1 In CAFM experiments the sample is usually fixed on the sample holder using a conductive tape or paste being silver paints the most widespread 4 A Faraday cage is also convenient to isolate the sample from any external electrical interference Using this setup when a potential difference is imposed between tip and sample an electrical field is generated which results in a net current flowing from tip to sample or vice versa The currents collected by the CAFM obey the relationship I J A e f f displaystyle I J cdot A eff nbsp where I is the total current flowing through the tip sample nanojunction J is the current density and Aeff is the effective emission area through which electrons can flow from now on we will refer to it just as effective area 1 The most common mistake in CAFM research is to assume that the effective emission area Aeff equals the physical contact area Ac Strictly this assumption is erroneous because in many different tip sample systems the electrical field applied may propagate laterally For example when the CAFM tip is placed on a metal the lateral conductivity of the sample is very high making in principle the whole sample surface area electrically connected Aeff equals the area covered by the metallic film electrode 5 6 Aeff has been defined as the sum of all those infinitesimal spatial locations on the surface of the sample that are electrically connected to the CAFM tip the potential difference is negligible As such Aeff is a virtual entity that summarizes all electrically relevant effects within the tip sample contact system into a single value over which the current density is assumed to be constant 1 Therefore when the CAFM tip is placed in contact with a metal a metallic sample or just a metallic pad on an insulator the lateral conductivity of the metal is very high and the CAFM tip can be understood as a current collector nanosized probe station 1 5 6 on the contrary if the CAFM tip is placed directly on an insulator it acts as a nanosized electrode and provides a very high lateral resolution The value of Aeff when a Pt Ir coated tip with a typical radius of 20 nm is placed on a SiO2 insulating film has been calculated to be typically 50 nm2 7 8 9 10 11 12 13 The value of Aeff can fluctuate depending on the environmental conditions and it can range from 1 nm2 in ultra high vacuum UHV to 300 nm2 in very humid environments 14 15 16 On well defined single crystal surfaces under UHV conditions it has even been demonstrated that measurements of the local conductivity with atomic resolution are possible 17 Applications edit nbsp Visualization of conductive filaments in HfO2 thin films for RRAM memories via CAFM CAFM was initially used in the field of nanoelectronics to monitor the electrical properties of thin dielectrics with very high lateral resolution The first CAFM development in 1993 had the goal of studying the local tunneling currents through 12 nm thick SiO2 films 3 In 1995 and 1996 O Shea 18 and Ruskell 19 further improved the lateral resolution of the CAFM technique achieving values of 10 nm and 8 nm respectively This enhanced resolution allowed to observe the first topographic current correlations and the inhomogeneity observed in the current maps was associated to the presence of local native defects in the oxide Following works by Olbrich 20 21 22 and Ebersberger 23 reported that in SiO2 films thinner than 5 nm the tunneling current increases exponentially with thickness reductions Consequently thickness fluctuations of tenths of nanometer in the SiO2 film could create electrically weak spots that reduce the reliability of the whole dielectric film as the dielectric breakdown BD is a stochastic process The capability of the CAFM for determining the thickness of thin oxides was further demonstrated by Frammelsberger and co workers 7 24 who statistically analyzed more than 7200 I V curves and reported SiO2 thicknesses with a sensitivity of 0 3 nm Other local phenomena like charge trapping 25 trap assisted tunneling 26 27 28 29 30 31 and stress induced leakage current SILC 32 can be also easily monitored with CAFM In general the CAFM can monitor the effect of any process that introduces local changes in the structure of the dielectric including thermal annealing 33 34 12 35 36 16 37 dopping 38 and irradiation 39 40 41 among others nbsp Number of publications and citations referring to CAFM per year up to June 14th of 2016 source Web of Science Apart from monitoring the electrical properties of a dielectric the CAFM can be also used to alter its properties by applying an electrical field locally In particular the CAFM is especially useful to determine which locations of the samples lead to premature BD which can provide essential information about the reliability of the samples The CAFM also helped to confirm the percolation theory of the BD by experimentally proving that this is a very local phenomenon that occurs in small areas typically below 100 nm2 32 Lateral propagations of the BD event can also be detected by CAFM 15 42 43 The severity of the BD event can also be studied from the dielectric breakdown induced epitaxy 26 44 45 46 which can be observed from subsequent topographic images collected with the CAFM after the voltage ramp Similarly the analysis of the BD recovery resistive switching RS can also be monitored by CAFM 47 48 49 50 All the capabilities of the CAFM for studying resistive switching in dielectrics have been summarized in the review article of reference 51 Unlike a normal AFM the CAFM can be also used to perform local photolithography via bias assisted local anodic oxidation LAO Nowadays the CAFM technique has expanded to many other fields of science including physics materials science chemistry and engineering among many others and it has been used to study different materials and or structures including nanoparticles 52 53 molecules 54 nanowires 55 carbon nanotubes 56 two dimensional 2D materials 57 58 59 60 61 coatings 62 63 64 photoelectricity 65 and piezoelectricity 66 among others As of June 14 of 2016 the CAFM had been used in 1325 journal research articles and it has become a popular tool in nanosciences 1 CAFM probes edit nbsp Left Standard metal varnished nanoprobe for CAFM Right Standard metal varnished nanoprobe for CAFM coated with a thin film of single layer graphene Center Schematic of the graphene coated nanoprobe The main problem of the CAFM is that the probes are more expensive and wear out faster than those used in topographic AFM maps mainly due to the high current densities flowing through the tip sample nanojunction but also due to lateral friction The premature degradation of a CAFM tip not only increases the cost of the experiments but also reduces the reliability of the data collected For this reason when using CAFM tip conductivity characterization using a reference sample before and after the experiments is highly recommended only if the CAFM tip holds the same conductivity before and after is the data collected considered reliable The first types of conductive nanoprobes used in CAFM experiments which are still widely used nowadays consist on standard silicon nanoprobes as those used in topographic AFM measurements varnished with thin metallic films including Pt Au Ru Ti and Cr among others 3 7 67 The varnish should be thick enough to withstand the large current densities and frictions and at the same time thin enough to not increase significantly the radius of the tip apex maintaining its sharpness and ensuring a high lateral resolution of the CAFM technique As mentioned the lifetime of the metal varnished tips for CAFM experiments is much shorter than in any other AFM mode mainly due to metallic varnish melting and loss of tip mass during the scans To solve this problem CAFM silicon tips varnished with hard materials like phosphorus doped diamond have appeared 67 The main problems of diamond coapted CAFM tips are i they are much more expensive and ii they are very stiff and can damage scratch the surface of the samples under tests Another option is to use sharpened metallic wires as the tip but also the use of hone techniques increases their price compared to metal coated Si tips Furthermore these tips can also degrade lose their conductivity by particle adhesion A cheap and effective methodology to protect CAFM tips from degrading is to coat them with graphene which can withstand well the high current densities and mechanical friction Moreover graphene is inert and slows down particle adhesion to the tip apex The preamplifier edit nbsp Schematic of a basic current to voltage preamplifier for CAFM The analogical current signals flowing through the tip sample nanojunction are sent to the preamplifier which transforms them into digital voltages that can be read by the data acquisition DAQ card of the computer Many manufacturers integrate the preamplifier in the so called CAFM application module which is a removable component that can be fixed to the AFM usually very near to the tip to minimize the electrical noise to perform conductivity measurements Similarly many other modules allow AFMs to perform other operations like scanning capacitance microscopy SCM or scanning spreading resistance microscopy SSRM In most CAFM experiments the currents measured typically can range between a few picoamperes and hundreds of microamperes while the voltages readable by the DAQ card usually range between 3 V to 3V 68 Therefore the preamplifier needs to provide a very low noise and a high transimpedance gain Figure 2 shows the simplified schematic of a typical low noise preamplifier for CAFM measurements 69 in which some elements can be distinguished i an operational amplifier with high input impedance ii a feedback resistor Rf and its parasite capacitor Cs and Johnson noise et associated effects iii a noise voltage source associated to the operational amplifier en and iv a capacitance associated to the input interconnections Ci A correct selection of the electrical components is essential to achieve good and reliable CAFM data acquisition For example the value of Rf is not trivial a very high value of Rf improves the noise signal ratio while reduces the bandwidth of the preamplifier Therefore the value of Rf should be chosen to provide enough bandwidth and a noise level below the current values that we want to measure The parameter en can be easily reduced by using a commercial low noise operational amplifier The capacitance associated to the connections Ci can be easily minimized by placing the preamplifier as near as possible to the conductive tip The company FEMTO one of the world leading manufacturers of preamplifiers compatible with CAFMs can provide devices with electrical noise as low as 3 fA and a gain up to 1013 V A 70 Nevertheless the main limitation of CAFM preamplifiers is their narrow current dynamic range which usually allows collecting electrical signals only within three or four orders of magnitude or even less To solve this problem preamplifiers with an adjustable gain can be used to focus on specific ranges 70 A more sophisticated solution for this problem is to combine the CAFM with a sourcemeter 71 72 semiconductor parameter analyzer or with a logarithmic preamplifier 73 which can capture the currents flowing through the tip sample system at any range and with a high resolution References edit a b c d e f Lanza Mario 2017 Conductive Atomic Force Microscopy Berlin Germany Wiley VCH p 400 ISBN 978 3 527 34091 0 PeakForce TUNA Bruker AFM Probes www brukerafmprobes com Retrieved 2017 02 04 a b c Murrell M P Welland M E O Shea S J Wong T M H Barnes J R McKinnon A W Heyns M Verhaverbeke S 1993 02 15 Spatially resolved electrical measurements of SiO2 gate oxides using atomic force microscopy Applied Physics Letters 62 7 786 788 Bibcode 1993ApPhL 62 786M doi 10 1063 1 108579 ISSN 0003 6951 Silver Paints Pastes SPI Supplies www 2spi com Retrieved 2017 02 04 a b Rommel Mathias Jambreck Joachim D Lemberger Martin Bauer Anton J Frey Lothar Murakami Katsuhisa Richter Christoph Weinzierl Philipp 2012 11 29 Influence of parasitic capacitances on conductive AFM I V measurements and approaches for its reduction Journal of Vacuum Science amp Technology B Nanotechnology and Microelectronics Materials Processing Measurement and Phenomena 31 1 01A108 Bibcode 2013JVSTB 31aA108R doi 10 1116 1 4768679 ISSN 2166 2746 a b Yanev V Erlbacher T Rommel M Bauer A J Frey L July 2009 Comparative study between conventional macroscopic IV techniques and advanced AFM based methods for electrical characterization of dielectrics at the nanoscale Microelectronic Engineering 86 7 9 1911 1914 doi 10 1016 j mee 2009 03 094 a b c Frammelsberger Werner Benstetter Guenther Kiely Janice Stamp Richard 2007 01 30 C AFM based thickness determination of thin and ultra thin SiO2 films by use of different conductive coated probe tips Applied Surface Science 253 7 3615 3626 Bibcode 2007ApSS 253 3615F doi 10 1016 j apsusc 2006 07 070 Zhang Kai Lanza Mario Shen Ziyong Fu Qiang Hou Shimin Porti Marc Nafria Montserrat 2014 05 04 Analysis of Factors in the Nanoscale Physical and Electrical Characterization of High K Materials by Conductive Atomic Force Microscope Integrated Ferroelectrics 153 1 1 8 Bibcode 2014InFer 153 1Z doi 10 1080 10584587 2014 902280 ISSN 1058 4587 S2CID 94116742 Pirrotta Onofrio Larcher Luca Lanza Mario Padovani Andrea Porti Marc Nafria Montserrat Bersuker Gennadi 2013 10 01 Leakage current through the poly crystalline HfO2 Trap densities at grains and grain boundaries Journal of Applied Physics 114 13 134503 134503 5 Bibcode 2013JAP 114m4503P doi 10 1063 1 4823854 ISSN 0021 8979 Lanza M Porti M Nafria M Aymerich X Sebastiani A Ghidini G Vedda A Fasoli M 2009 12 01 Combined Nanoscale and Device Level Degradation Analysis of Layers of MOS Nonvolatile Memory Devices IEEE Transactions on Device and Materials Reliability 9 4 529 536 doi 10 1109 TDMR 2009 2027228 ISSN 1530 4388 S2CID 28464435 Lanza M Porti M Nafria M Aymerich X Ghidini G Sebastiani A September 2009 Trapped charge and stress induced leakage current SILC in tunnel SiO2 layers of de processed MOS non volatile memory devices observed at the nanoscale Microelectronics Reliability 49 9 11 1188 1191 doi 10 1016 j microrel 2009 06 016 a b Lanza M Porti M Nafria M Aymerich X Benstetter G Lodermeier E Ranzinger H Jaschke G Teichert S Wilde L Michalowski P July 2009 Crystallization and silicon diffusion nanoscale effects on the electrical properties of Al2O3 based devices Microelectronic Engineering 86 7 9 1921 1924 doi 10 1016 j mee 2009 03 020 Lanza M Porti M Nafria M Benstetter G Frammelsberger W Ranzinger H Lodermeier E Jaschke G September 2007 Influence of the manufacturing process on the electrical properties of thin lt 4 nm Hafnium based high k stacks observed with CAFM Microelectronics Reliability 47 9 11 1424 1428 doi 10 1016 j microrel 2007 07 045 Lanza M Porti M Nafria M Aymerich X Whittaker E Hamilton B 2010 10 01 Note Electrical resolution during conductive atomic force microscopy measurements under different environmental conditions and contact forces Review of Scientific Instruments 81 10 106110 106110 3 Bibcode 2010RScI 81j6110L doi 10 1063 1 3491956 ISSN 0034 6748 PMID 21034138 a b Lanza M Porti M Nafria M Aymerich X Whittaker E Hamilton B September 2010 UHV CAFM characterization of high k dielectrics Effect of the technique resolution on the pre and post breakdown electrical measurements Microelectronics Reliability 50 9 11 1312 1315 doi 10 1016 j microrel 2010 07 049 a b Lanza Mario Iglesias Vanessa Porti Marc Nafria Montse Aymerich Xavier 2011 01 31 Polycrystallization effects on the nanoscale electrical properties of high k dielectrics Nanoscale Research Letters 6 1 108 Bibcode 2011NRL 6 108L doi 10 1186 1556 276x 6 108 ISSN 1556 276X PMC 3211152 PMID 21711617 Rodenbucher C Bihlmayer G Speier W Kubacki J Wojtyniak M Rogala M Wrana D Krok F Szot K 2018 Local surface conductivity of transition metal oxides mapped with true atomic resolution Nanoscale 10 24 11498 11505 arXiv 1611 07773 doi 10 1039 C8NR02562B PMID 29888770 S2CID 47013247 O Shea S J Atta R M Murrell M P Welland M E 1995 09 01 Conducting atomic force microscopy study of silicon dioxide breakdown Journal of Vacuum Science amp Technology B Microelectronics and Nanometer Structures Processing Measurement and Phenomena 13 5 1945 1952 Bibcode 1995JVSTB 13 1945O doi 10 1116 1 588113 ISSN 1071 1023 Ruskell Todd G Workman Richard K Chen Dong Sarid Dror Dahl Sarah Gilbert Stephen 1996 01 01 High resolution Fowler Nordheim field emission maps of thin silicon oxide layers Applied Physics Letters 68 1 93 95 Bibcode 1996ApPhL 68 93R doi 10 1063 1 116782 ISSN 0003 6951 Olbrich A Ebersberger B Boit C 1998 03 01 Nanoscale electrical characterization of thin oxides with conducting atomic force microscopy 1998 IEEE International Reliability Physics Symposium Proceedings 36th Annual Cat No 98CH36173 RELPHY 98 pp 163 168 doi 10 1109 RELPHY 1998 670490 ISBN 978 0 7803 4400 6 S2CID 110367701 Olbrich Alexander Ebersberger Bernd Boit Christian 1998 11 19 Conducting atomic force microscopy for nanoscale electrical characterization of thin SiO2 Applied Physics Letters 73 21 3114 3116 Bibcode 1998ApPhL 73 3114O doi 10 1063 1 122690 ISSN 0003 6951 Olbrich Alexander Ebersberger Bernd Boit Christian Vancea J Hoffmarm H June 1999 A new AFM based tool for testing dielectric quality and reliability on a nanometer scale Microelectronics Reliability 39 6 7 941 946 doi 10 1016 S0026 2714 99 00127 4 Ebersberger B Boit C Benzinger H Gunther E 1996 04 01 Thickness mapping of thin dielectrics with emission microscopy and conductive atomic force microscopy for assessment of dielectrics reliability Proceedings of International Reliability Physics Symposium RELPHY 96 pp 126 130 doi 10 1109 RELPHY 1996 492072 ISBN 978 0 7803 2753 5 S2CID 109344701 Frammelsberger Werner Benstetter Guenther Kiely Janice Stamp Richard 2006 Thickness determination of thin and ultra thin SiO2 films by C AFM IV spectroscopy Applied Surface Science 252 6 2375 2388 Bibcode 2006ApSS 252 2375F doi 10 1016 j apsusc 2005 04 010 Polspoel W Vandervorst W March 2007 Evaluation of trap creation and charging in thin SiO2 using both SCM and C AFM Microelectronic Engineering 84 3 495 500 doi 10 1016 j mee 2006 10 074 a b Nasyrov K A Shaimeev S S Gritsenko V A 2009 12 24 Trap assisted tunneling hole injection in SiO2 Experiment and theory Journal of Experimental and Theoretical Physics 109 5 786 Bibcode 2009JETP 109 786N doi 10 1134 S1063776109110089 ISSN 1063 7761 S2CID 122592036 Fiorenza Patrick Polspoel Wouter Vandervorst Wilfried 2006 05 29 Conductive atomic force microscopy studies of thin SiO2 layer degradation Applied Physics Letters 88 22 222104 Bibcode 2006ApPhL 88v2104F doi 10 1063 1 2208370 ISSN 0003 6951 Wu You Lin Lin Shi Tin 2006 03 01 Two trap assisted tunneling model for post breakdown I V characteristics in ultrathin silicon dioxide IEEE Transactions on Device and Materials Reliability 6 1 75 80 doi 10 1109 TDMR 2006 870351 ISSN 1530 4388 Pakes C I Ramelow S Prawer S Jamieson D N 2004 04 13 Nanoscale electrical characterization of trap assisted quasibreakdown fluctuations in SiO2 Applied Physics Letters 84 16 3142 3144 Bibcode 2004ApPhL 84 3142P doi 10 1063 1 1712033 ISSN 0003 6951 Degraeve R Kaczer B Schuler F Lorenzini M Wellekens D Hendrickx P Houdt J Van Haspeslagh L Tempel G 2001 12 01 Statistical model for stress induced leakage current and pre breakdown current jumps in ultra thin oxide layers International Electron Devices Meeting Technical Digest Cat No 01CH37224 pp 6 2 1 6 2 4 doi 10 1109 IEDM 2001 979447 ISBN 978 0 7803 7050 0 S2CID 27991853 Porti M Nafria M Aymerich X Olbrich A Ebersberger B 2002 01 29 Electrical characterization of stressed and broken down SiO2 films at a nanometer scale using a conductive atomic force microscope Journal of Applied Physics 91 4 2071 2079 Bibcode 2002JAP 91 2071P doi 10 1063 1 1430542 ISSN 0021 8979 a b Tan Tingting Liu Zhengtang Tian Hao Liu Wenting 2010 07 25 Low voltage stress induced leakage current in HfO2 dielectric films Materials Science and Engineering B 171 1 3 159 161 doi 10 1016 j mseb 2010 03 091 Ang D S Ong Y C O Shea S J Pey K L Tung C H Kawanago T Kakushima K Iwai H 2008 05 12 Polarity dependent breakdown of the high k SiOx gate stack A phenomenological explanation by scanning tunneling microscopy Applied Physics Letters 92 19 192904 Bibcode 2008ApPhL 92s2904A doi 10 1063 1 2926655 ISSN 0003 6951 Lu X B Zhang X Huang R Lu H B Chen Z H Zhou H W Wang X P Nguyen B Y Wang C Z 2004 10 01 Effect of post annealing on the physical and electrical properties of LaAlO Sub 3 Gate dielectrics Proceedings 7th International Conference on Solid State and Integrated Circuits Technology 2004 Vol 1 pp 419 422 vol 1 doi 10 1109 ICSICT 2004 1435039 ISBN 978 0 7803 8511 5 S2CID 25239456 Lanza M Porti M Nafria M Aymerich X Benstetter G Lodermeier E Ranzinger H Jaschke G Teichert S 2011 03 01 Conductivity and Charge Trapping After Electrical Stress in Amorphous and Polycrystalline Devices Studied With AFM Related Techniques IEEE Transactions on Nanotechnology 10 2 344 351 Bibcode 2011ITNan 10 344L doi 10 1109 TNANO 2010 2041935 ISSN 1536 125X S2CID 28810246 Bayerl A Lanza M Porti M Nafria M Aymerich X Campabadal F Benstetter G 2011 09 01 Nanoscale and Device Level Gate Conduction Variability of High k Dielectrics Based Metal Oxide Semiconductor Structures IEEE Transactions on Device and Materials Reliability 11 3 495 501 doi 10 1109 TDMR 2011 2161087 ISSN 1530 4388 S2CID 22874323 Bayerl Albin Lanza Mario Aguilera Lidia Porti Marc Nafria Montserrat Aymerich Xavier Gendt Stefan de June 2013 Nanoscale and device level electrical behavior of annealed ALD Hf based gate oxide stacks grown with different precursors Microelectronics Reliability 53 6 867 871 doi 10 1016 j microrel 2013 02 005 Muenstermann Ruth Menke Tobias Dittmann Regina Mi Shaobo Jia Chun Lin Park Daesung Mayer Joachim 2010 12 15 Correlation between growth kinetics and nanoscale resistive switching properties of SrTiO3 thin films Journal of Applied Physics 108 12 124504 124504 8 Bibcode 2010JAP 108l4504M doi 10 1063 1 3520674 ISSN 0021 8979 Wu Y L Lin S T Chang T M Liou J J 2007 06 01 Nanoscale Bias Annealing Effect in Postirradiated Thin Silicon Dioxide Films Observed by Conductive Atomic Force Microscopy IEEE Transactions on Device and Materials Reliability 7 2 351 355 doi 10 1109 TDMR 2007 901069 ISSN 1530 4388 S2CID 23406644 Wu You Lin Lin Shi Tin Chang Tsung Min Liou Juin J February 2007 Reliability study of ultrathin oxide films subject to irradiation then stress treatment using conductive atomic force microscopy Microelectronics Reliability 47 2 3 419 421 doi 10 1016 j microrel 2006 05 014 Porti M Nafria N Gerardin S Aymerich X Cester A Paccagnella A Ghidini G 2009 01 01 Implanted and irradiated SiO2 Si structure electrical properties at the nanoscale Journal of Vacuum Science amp Technology B Microelectronics and Nanometer Structures Processing Measurement and Phenomena 27 1 421 425 Bibcode 2009JVSTB 27 421P doi 10 1116 1 3043475 ISSN 1071 1023 Blasco X Nafria M Aymerich X Vandervorst W 2005 Comparison of SiO2 and HfO2 SiO2 gate stacks electrical behaviour at a nanometre scale with CAFM Electronics Letters 41 12 719 Bibcode 2005ElL 41 719B doi 10 1049 el 20050805 Wu You Lin Lin Shi Tin February 2008 Breakdown spots propagation in ultra thin SiO2 films under repetitive ramped voltage stress using conductive atomic force microscopy Journal of Physics and Chemistry of Solids 69 2 3 470 474 Bibcode 2008JPCS 69 470W doi 10 1016 j jpcs 2007 07 077 Tung C H Pey K L Lin W H Radhakrishnan M K 2002 09 01 Polarity dependent dielectric breakdown induced epitaxy DBIE in Si MOSFETs IEEE Electron Device Letters 23 9 526 528 Bibcode 2002IEDL 23 526T doi 10 1109 LED 2002 802662 ISSN 0741 3106 Polspoel W Favia P Mody J Bender H Vandervorst W 2009 07 15 Physical degradation of gate dielectrics induced by local electrical stress using conductive atomic force microscopy Journal of Applied Physics 106 2 024101 024101 7 Bibcode 2009JAP 106b4101P doi 10 1063 1 3153965 ISSN 0021 8979 Porti M Nafria M Blum M C Aymerich X Sadewasser S 2003 06 10 Atomic force microscope topographical artifacts after the dielectric breakdown of ultrathin SiO2 films Surface Science 532 535 727 731 Bibcode 2003SurSc 532 727P doi 10 1016 S0039 6028 03 00150 X Lanza M Bersuker G Porti M Miranda E Nafria M Aymerich X 2012 11 05 Resistive switching in hafnium dioxide layers Local phenomenon at grain boundaries Applied Physics Letters 101 19 193502 Bibcode 2012ApPhL 101s3502L doi 10 1063 1 4765342 ISSN 0003 6951 Lanza M Zhang K Porti M Nafria M Shen Z Y Liu L F Kang J F Gilmer D Bersuker G 2012 03 19 Grain boundaries as preferential sites for resistive switching in the HfO2 resistive random access memory structures Applied Physics Letters 100 12 123508 Bibcode 2012ApPhL 100l3508L doi 10 1063 1 3697648 ISSN 0003 6951 Shi Yuanyuan Ji Yanfeng Hui Fei Nafria Montserrat Porti Marc Bersuker Gennadi Lanza Mario 2015 04 01 In Situ Demonstration of the Link Between Mechanical Strength and Resistive Switching in Resistive Random Access Memories Advanced Electronic Materials 1 4 n a doi 10 1002 aelm 201400058 ISSN 2199 160X S2CID 110305072 Shi Yuanyuan Ji Yanfeng Hui Fei Iglesias Vanessa Porti Marc Nafria Montserrat Miranda Enrique Bersuker Gennadi Lanza Mario 2014 08 08 Invited Elucidating the Origin of Resistive Switching in Ultrathin Hafnium Oxides through High Spatial Resolution Tools ECS Transactions 64 14 19 28 Bibcode 2014ECSTr 64n 19S doi 10 1149 06414 0019ecst ISSN 1938 6737 Lanza Mario 2014 03 13 A Review on Resistive Switching in High k Dielectrics A Nanoscale Point of View Using Conductive Atomic Force Microscope Materials 7 3 2155 2182 Bibcode 2014Mate 7 2155L doi 10 3390 ma7032155 PMC 5453275 PMID 28788561 Sze J Y Tay B K Pakes C I Jamieson D N Prawer S 2005 09 15 Conducting Ni nanoparticles in an ion modified polymer Journal of Applied Physics 98 6 066101 066101 3 Bibcode 2005JAP 98f6101S doi 10 1063 1 2014938 ISSN 0021 8979 Shi Yuanyuan Ji Yanfeng Sun Hui Hui Fei Hu Jianchen Wu Yaxi Fang Jianlong Lin Hao Wang Jianxiang 2015 07 16 Nanoscale characterization of PM2 5 airborne pollutants reveals high adhesiveness and aggregation capability of soot particles Scientific Reports 5 11232 Bibcode 2015NatSR 511232S doi 10 1038 srep11232 ISSN 2045 2322 PMC 4503936 PMID 26177695 Cui X D Primak A Zarate X Tomfohr J Sankey O F Moore A L Moore T A Gust D Harris G 2001 10 19 Reproducible Measurement of Single Molecule Conductivity Science 294 5542 571 574 Bibcode 2001Sci 294 571C doi 10 1126 science 1064354 ISSN 0036 8075 PMID 11641492 S2CID 26028013 Wang Zhong Lin Song Jinhui 2006 04 14 Piezoelectric Nanogenerators Based on Zinc Oxide Nanowire Arrays Science 312 5771 242 246 Bibcode 2006Sci 312 242W doi 10 1126 science 1124005 ISSN 0036 8075 PMID 16614215 S2CID 4810693 Zhou Chongwu Kong Jing Dai Hongjie 2000 03 14 Electrical measurements of individual semiconducting single walled carbon nanotubes of various diameters Applied Physics Letters 76 12 1597 1599 Bibcode 2000ApPhL 76 1597Z doi 10 1063 1 126107 ISSN 0003 6951 S2CID 17973840 Iglesias V Porti M Nafria M Aymerich X Dudek P Schroeder T Bersuker G 2010 12 27 Correlation between the nanoscale electrical and morphological properties of crystallized hafnium oxide based metal oxide semiconductor structures Applied Physics Letters 97 26 262906 Bibcode 2010ApPhL 97z2906I doi 10 1063 1 3533257 ISSN 0003 6951 Vecchio Carmelo Sonde Sushant Bongiorno Corrado Rambach Martin Yakimova Rositza Raineri Vito Giannazzo Filippo 2011 03 29 Nanoscale structural characterization of epitaxial graphene grown on off axis 4H SiC 0001 Nanoscale Research Letters 6 1 269 Bibcode 2011NRL 6 269V doi 10 1186 1556 276x 6 269 ISSN 1556 276X PMC 3211332 PMID 21711803 Giannazzo Filippo Sonde Sushant Rimini Emanuele Raineri Vito 2011 01 31 Lateral homogeneity of the electronic properties in pristine and ion irradiated graphene probed by scanning capacitance spectroscopy Nanoscale Research Letters 6 1 109 Bibcode 2011NRL 6 109G doi 10 1186 1556 276x 6 109 ISSN 1556 276X PMC 3211153 PMID 21711643 Ji Yanfeng Pan Chengbin Zhang Meiyun Long Shibing Lian Xiaojuan Miao Feng Hui Fei Shi Yuanyuan Larcher Luca Wu Ernest Lanza Mario 2016 01 04 Boron nitride as two dimensional dielectric Reliability and dielectric breakdown Applied Physics Letters 108 1 012905 Bibcode 2016ApPhL 108a2905J doi 10 1063 1 4939131 ISSN 0003 6951 Lanza Mario Wang Yan Gao Teng Bayerl Albin Porti Marc Nafria Montserrat Zhou Yangbo Jing Guangyin Zhang Yanfeng 2013 05 21 Electrical and mechanical performance of graphene sheets exposed to oxidative environments Nano Research 6 7 485 495 doi 10 1007 s12274 013 0326 6 ISSN 1998 0124 S2CID 97263039 Tan Susheng Tang Zhiyong Liang Xiaorong Kotov Nicholas A 2004 09 01 Resonance Tunneling Diode Structures on CdTe Nanowires Made by Conductive AFM Nano Letters 4 9 1637 1641 Bibcode 2004NanoL 4 1637T doi 10 1021 nl0492077 ISSN 1530 6984 Jiang Lanlan Xiao Na Wang Bingru Grustan Gutierrez Enric Jing Xu Babor Petr Kolibal Miroslav Lu Guangyuan Wu Tianru 2017 01 26 High resolution characterization of hexagonal boron nitride coatings exposed to aqueous and air oxidative environments Nano Research 10 6 2046 2055 doi 10 1007 s12274 016 1393 2 ISSN 1998 0124 S2CID 99473899 Shi Yuanyuan Ji Yanfeng Hui Fei Wu Hai Hua Lanza Mario 2014 09 04 Ageing mechanisms and reliability of graphene based electrodes Nano Research 7 12 1820 1831 doi 10 1007 s12274 014 0542 8 ISSN 1998 0124 S2CID 54516801 Howell Sarah L Padalkar Sonal Yoon KunHo Li Qiming Koleske Daniel D Wierer Jonathan J Wang George T Lauhon Lincoln J 2013 11 13 Spatial Mapping of Efficiency of GaN InGaN Nanowire Array Solar Cells Using Scanning Photocurrent Microscopy Nano Letters 13 11 5123 5128 Bibcode 2013NanoL 13 5123H doi 10 1021 nl402331u ISSN 1530 6984 PMID 24099617 Pan Chengbin Hu Jianchen Grustan Gutierrez Enric Hoang Minh Tuan Duan Huiling Yvonnet Julien Mitrushchenkov Alexander Chambaud Gilberte Lanza Mario 2016 04 21 Suppression of nanowire clustering in hybrid energy harvesters J Mater Chem C 4 16 3646 3653 doi 10 1039 c6tc00468g ISSN 2050 7534 a b NanoWorld National Instriuments Tiedje T Brown A 1990 07 15 Performance limits for the scanning tunneling microscope Journal of Applied Physics 68 2 649 654 Bibcode 1990JAP 68 649T doi 10 1063 1 346794 ISSN 0021 8979 a b FEMTO Retrieved 4 February 2016 Lanza M Bayerl A Gao T Porti M Nafria M Jing G Y Zhang Y F Liu Z F Duan H L 2013 03 13 Graphene Coated Atomic Force Microscope Tips for Reliable Nanoscale Electrical Characterization Advanced Materials 25 10 1440 1444 Bibcode 2013AdM 25 1440L doi 10 1002 adma 201204380 ISSN 1521 4095 PMID 23280635 S2CID 205248208 Hui Fei Vajha Pujashree Shi Yuanyuan Ji Yanfeng Duan Huiling Padovani Andrea Larcher Luca Li Xiao Rong Lanza Mario 2016 04 21 Moving graphene devices from lab to market advanced graphene coated nanoprobes Nanoscale 8 16 8466 8473 Bibcode 2016Nanos 8 8466H doi 10 1039 c5nr06235g ISSN 2040 3372 PMID 26593053 Aguilera L Lanza M Porti M Grifoll J Nafria M Aymerich X 2008 07 01 Improving the electrical performance of a conductive atomic force microscope with a logarithmic current to voltage converter Review of Scientific Instruments 79 7 073701 073701 5 Bibcode 2008RScI 79g3701A doi 10 1063 1 2952058 ISSN 0034 6748 PMID 18681702 Retrieved from https en wikipedia org w index php title Conductive atomic force microscopy amp oldid 1188064327, wikipedia, wiki, book, books, library,

article

, read, download, free, free download, mp3, video, mp4, 3gp, jpg, jpeg, gif, png, picture, music, song, movie, book, game, games.