Spark testing is a method of determining the general classification of ferrous materials. It normally entails taking a piece of metal, usually scrap, and applying it to a grinding wheel in order to observe the sparks emitted.[1] These sparks can be compared to a chart or to sparks from a known test sample to determine the classification. Spark testing also can be used to sort ferrous materials, establishing the difference from one another by noting whether the spark is the same or different.

Spark testing of tool steel
Spark testing of mild steel

Spark testing is used because it is quick, easy, and inexpensive. Moreover, test samples do not have to be prepared in any way, so, often, a piece of scrap is used. The main disadvantage to spark testing is its inability to identify a material positively; if positive identification is required, chemical analysis must be used.[2] The spark comparison method also damages the material being tested, at least slightly.

Spark testing most often is used in tool rooms, machine shops, heat treating shops, and foundries.[3]

Process edit

A bench grinder is usually used to create the sparks, but sometimes this is not convenient, so a portable grinder is used. In either case, the grinding wheel must have adequate surface velocity, at least 23 m/s (4500 surface feet per minute (sfpm)), but should be between 38 and 58 m/s (7500–11,500 sfpm). The wheel should be coarse and hard, therefore aluminium oxide or carborundum often are employed. The test area should be in an area where there is no bright light shining directly into the observer's eyes. Moreover, the grinding wheel and surrounding area should be dark so that the sparks can be observed clearly. The test sample is then touched lightly to the grinding wheel to produce the sparks.[1][2]

The important spark characteristics are color, volume, nature of the spark, and length. Note that the length is dependent on the amount of pressure applied to the grinding wheel, so this can be a poor comparison tool if the pressure is not exactly the same for the samples. Also, the grinding wheel must be dressed frequently to remove metallic build-up.[1][2]

Compressed air method edit

Another less common method for creating sparks is heating up the sample to red heat and then applying compressed air to the sample. The compressed air supplies enough oxygen to ignite the sample and give off sparks. This method is more accurate than using a grinder because it will always give off sparks of the same length for the same sample. The compressed air applies in essence the same "pressure" each time. This makes observations of the spark length a much more reliable characteristic for comparison.[4]

Automated spark testing edit

Automated spark testing has been developed to remove the reliance upon operator skill and experience, thereby increasing reliability. The system relies upon spectroscopy, spectrometry, and other methods to "observe" the spark pattern. It has been found that this system can determine the difference between two materials that give off sparks that are indistinguishable to the human eye.[2]

Spark characteristics edit

 
(A) High-carbon steel
(B) Manganese steel
(C) Tungsten steel
(D) Molybdenum steel
 
(A) Wrought iron
(B) Mild steel
(C) Steel with 0.5 to 0.85% carbon
(D) High-carbon tool steel
(E) High-speed steel
(F) Manganese steel
(G) Mushet steel
(H) Special magnet steel
Wrought iron
Wrought iron sparks flow out in straight lines. The tails of the sparks widen out near the end, similar to a leaf.[1][5]
Mild steel
Mild steel sparks are similar to wrought iron's, except they will have tiny forks and their lengths will vary more. The sparks will be white in color.[1][5]
Medium-carbon steel
This steel has more forking than mild steel and a wide variety of spark lengths, with more near the grinding wheel.[5]
High-carbon steel
High-carbon steel has a bushy spark pattern (much forking) that starts at the grinding wheel. The sparks are not as bright as the medium-carbon steel ones.[5]
Manganese steel
Manganese steel has medium length sparks that fork twice before ending.[5]
High-speed steel
High-speed steel has a faint red spark that sparks at the tip.[5]
300-series stainless steel
These sparks are not so dense as the carbon steel sparks, do not fork, and are orange to straw in color.[2]
310-series stainless steel
These sparks are much shorter and thinner than the 300-series sparks. They are red to orange in color and do not fork.[2]
400-series stainless steel
400-series sparks are similar to 300-series sparks, but are slightly longer and have forks at the ends of the sparks.[2]
Cast iron
Cast iron has very short sparks that begin at the grinding wheel.[1]
Nickel and cobalt high-temperature alloys
These sparks are thin and very short, they are dark-red in color, and do not fork.[2]
Cemented carbide
Cemented carbide has sparks under 3 inches, which are dark-red in color and do not fork.[6]
Titanium
Although titanium is a non-ferrous metal, it gives off a great deal of sparks. These sparks are easily distinguishable from ferrous metals, as they are a very brilliant, blinding, white color.[7]

History edit

In 1909,[8] Max Bermann, an engineer in Budapest, was the first to discover that spark testing can be used reliably to classify ferrous material. He originally claimed to be able to distinguish different types of ferrous materials based on percent carbon and principal alloying elements. Moreover, he claimed to achieve an accuracy of 0.01% carbon content.[3][9]

Tschorn [10] produced an exhaustive treatment of spark testing. His book, Spark Atlas of Steels, along with Spark Testing by Gladwin represent the two most comprehensive texts on the subject [11]

As of the late 1980s, the industrial use of spark testing is not as common as it used to be.[12] In the early 21st century the availability of portable X-ray fluorescence equipment largely superseded it in laboratory practice.

See also edit

References edit

  1. ^ a b c d e f Geary 1999, p. 63.
  2. ^ a b c d e f g h Davis & ASM International 1994, pp. 126–127.
  3. ^ a b The Engineering Magazine 1910, pp. 262–265.
  4. ^ Saunders 1908, pp. 4808–4810.
  5. ^ a b c d e f Lee 1996, p. 22.
  6. ^ Woodson, C. W. (September 1959), "Spark Streams Identify Metals", Popular Mechanics, 112 (3): 192–193, ISSN 0032-4558.
  7. ^ "Titanium, or Plain Ol Steel?". Retrieved 2011-02-21.
  8. ^ Max Bermann first reported the spark testing method at the fifth International Association for Testing Materials conference, which was held in Copenhagen, as reported by The Engineering Magazine. Based on knowing the conference was held in Copenhagen, the year can be found from:
    • "Copenhagen Congress on the Testing of Materials of Construction", Nature, 81 (2082): 377–378, 1909-10-23, Bibcode:1909Natur..81..377., doi:10.1038/081377a0.
    • François, D.; Pineau, André (2002), From Charpy to Present Impact Testing, Elsevier, p. 7, ISBN 978-0-08-043970-9
  9. ^ Oberg & Jones 1918, pp. 88–92.
  10. ^ Tschorn 1963.
  11. ^ Dulski 1996, p. 57.
  12. ^ Drozda et al. 1987, p. 7-18.

Bibliography edit

  • Davis, Joseph R; ASM International (1994), Stainless steels (2nd, Illustrated ed.), ASM International, ISBN 978-0-87170-503-7.
  • Dulski, Thomas R. (1996), A manual for the chemical analysis of metals, ASTM International, ISBN 978-0-80312-066-2.
  • Gladwin, W.M., Spark Testing, United Steel Co., Sheffield, UK.
  • Drozda, Tom; Wick, Charles; Benedict, John T.; Veilleux, Raymond F.; Bakerjian, Ramon (1987), Tool and manufacturing engineers handbook: Quality Control and Assembly, vol. 4, Society of Manufacturing Engineers, ISBN 0-87263-135-4.
  • The Engineering Magazine, vol. XXXVIII, Engineering Magazine Co., 1910.
  • Geary, Don (1999), Welding, McGraw-Hill Professional, ISBN 978-0-07-134245-2.
  • Lee, Leonard (1996), The Complete Guide to Sharpening, Taunton Press, ISBN 978-1-56158-125-2.
  • Oberg, Erik; Jones, Franklin Day (1918), Iron and Steel (1st ed.), The Industrial Press.
  • Saunders, William Lawrence (1908), Compressed Air Magazine, vol. XIII, Compressed Air Magazine Company.
  • Tschorn, Gerhart (1963), Spark Atlas of Steels: Cast-Iron, Pig-Iron, Ferro-Alloys and Metals, New York, The MacMillan Company.

External links edit

  • Spark test pictures of various materials

January 01, 1970
spark, testing, confused, with, streak, test, mineralogy, spark, testing, explosives, safety, testing, explosives, method, determining, general, classification, ferrous, materials, normally, entails, taking, piece, metal, usually, scrap, applying, grinding, wh. Not to be confused with Streak test mineralogy For spark testing explosives see Safety testing of explosives Spark testing is a method of determining the general classification of ferrous materials It normally entails taking a piece of metal usually scrap and applying it to a grinding wheel in order to observe the sparks emitted 1 These sparks can be compared to a chart or to sparks from a known test sample to determine the classification Spark testing also can be used to sort ferrous materials establishing the difference from one another by noting whether the spark is the same or different Spark testing of tool steel Spark testing of mild steel Spark testing is used because it is quick easy and inexpensive Moreover test samples do not have to be prepared in any way so often a piece of scrap is used The main disadvantage to spark testing is its inability to identify a material positively if positive identification is required chemical analysis must be used 2 The spark comparison method also damages the material being tested at least slightly Spark testing most often is used in tool rooms machine shops heat treating shops and foundries 3 Contents 1 Process 1 1 Compressed air method 1 2 Automated spark testing 2 Spark characteristics 3 History 4 See also 5 References 5 1 Bibliography 6 External linksProcess editA bench grinder is usually used to create the sparks but sometimes this is not convenient so a portable grinder is used In either case the grinding wheel must have adequate surface velocity at least 23 m s 4500 surface feet per minute sfpm but should be between 38 and 58 m s 7500 11 500 sfpm The wheel should be coarse and hard therefore aluminium oxide or carborundum often are employed The test area should be in an area where there is no bright light shining directly into the observer s eyes Moreover the grinding wheel and surrounding area should be dark so that the sparks can be observed clearly The test sample is then touched lightly to the grinding wheel to produce the sparks 1 2 The important spark characteristics are color volume nature of the spark and length Note that the length is dependent on the amount of pressure applied to the grinding wheel so this can be a poor comparison tool if the pressure is not exactly the same for the samples Also the grinding wheel must be dressed frequently to remove metallic build up 1 2 Compressed air method edit Another less common method for creating sparks is heating up the sample to red heat and then applying compressed air to the sample The compressed air supplies enough oxygen to ignite the sample and give off sparks This method is more accurate than using a grinder because it will always give off sparks of the same length for the same sample The compressed air applies in essence the same pressure each time This makes observations of the spark length a much more reliable characteristic for comparison 4 Automated spark testing edit Automated spark testing has been developed to remove the reliance upon operator skill and experience thereby increasing reliability The system relies upon spectroscopy spectrometry and other methods to observe the spark pattern It has been found that this system can determine the difference between two materials that give off sparks that are indistinguishable to the human eye 2 Spark characteristics edit nbsp A High carbon steel B Manganese steel C Tungsten steel D Molybdenum steel nbsp A Wrought iron B Mild steel C Steel with 0 5 to 0 85 carbon D High carbon tool steel E High speed steel F Manganese steel G Mushet steel H Special magnet steel Wrought iron Wrought iron sparks flow out in straight lines The tails of the sparks widen out near the end similar to a leaf 1 5 Mild steel Mild steel sparks are similar to wrought iron s except they will have tiny forks and their lengths will vary more The sparks will be white in color 1 5 Medium carbon steel This steel has more forking than mild steel and a wide variety of spark lengths with more near the grinding wheel 5 High carbon steel High carbon steel has a bushy spark pattern much forking that starts at the grinding wheel The sparks are not as bright as the medium carbon steel ones 5 Manganese steel Manganese steel has medium length sparks that fork twice before ending 5 High speed steel High speed steel has a faint red spark that sparks at the tip 5 300 series stainless steel These sparks are not so dense as the carbon steel sparks do not fork and are orange to straw in color 2 310 series stainless steel These sparks are much shorter and thinner than the 300 series sparks They are red to orange in color and do not fork 2 400 series stainless steel 400 series sparks are similar to 300 series sparks but are slightly longer and have forks at the ends of the sparks 2 Cast iron Cast iron has very short sparks that begin at the grinding wheel 1 Nickel and cobalt high temperature alloys These sparks are thin and very short they are dark red in color and do not fork 2 Cemented carbide Cemented carbide has sparks under 3 inches which are dark red in color and do not fork 6 Titanium Although titanium is a non ferrous metal it gives off a great deal of sparks These sparks are easily distinguishable from ferrous metals as they are a very brilliant blinding white color 7 History editIn 1909 8 Max Bermann an engineer in Budapest was the first to discover that spark testing can be used reliably to classify ferrous material He originally claimed to be able to distinguish different types of ferrous materials based on percent carbon and principal alloying elements Moreover he claimed to achieve an accuracy of 0 01 carbon content 3 9 Tschorn 10 produced an exhaustive treatment of spark testing His book Spark Atlas of Steels along with Spark Testing by Gladwin represent the two most comprehensive texts on the subject 11 As of the late 1980s the industrial use of spark testing is not as common as it used to be 12 In the early 21st century the availability of portable X ray fluorescence equipment largely superseded it in laboratory practice See also editFlame test Emission spectrumReferences edit a b c d e f Geary 1999 p 63 a b c d e f g h Davis amp ASM International 1994 pp 126 127 a b The Engineering Magazine 1910 pp 262 265 Saunders 1908 pp 4808 4810 a b c d e f Lee 1996 p 22 Woodson C W September 1959 Spark Streams Identify Metals Popular Mechanics 112 3 192 193 ISSN 0032 4558 Titanium or Plain Ol Steel Retrieved 2011 02 21 Max Bermann first reported the spark testing method at the fifth International Association for Testing Materials conference which was held in Copenhagen as reported by The Engineering Magazine Based on knowing the conference was held in Copenhagen the year can be found from Copenhagen Congress on the Testing of Materials of Construction Nature 81 2082 377 378 1909 10 23 Bibcode 1909Natur 81 377 doi 10 1038 081377a0 Francois D Pineau Andre 2002 From Charpy to Present Impact Testing Elsevier p 7 ISBN 978 0 08 043970 9 Oberg amp Jones 1918 pp 88 92 Tschorn 1963 Dulski 1996 p 57 Drozda et al 1987 p 7 18 Bibliography edit Davis Joseph R ASM International 1994 Stainless steels 2nd Illustrated ed ASM International ISBN 978 0 87170 503 7 Dulski Thomas R 1996 A manual for the chemical analysis of metals ASTM International ISBN 978 0 80312 066 2 Gladwin W M Spark Testing United Steel Co Sheffield UK Drozda Tom Wick Charles Benedict John T Veilleux Raymond F Bakerjian Ramon 1987 Tool and manufacturing engineers handbook Quality Control and Assembly vol 4 Society of Manufacturing Engineers ISBN 0 87263 135 4 The Engineering Magazine vol XXXVIII Engineering Magazine Co 1910 Geary Don 1999 Welding McGraw Hill Professional ISBN 978 0 07 134245 2 Lee Leonard 1996 The Complete Guide to Sharpening Taunton Press ISBN 978 1 56158 125 2 Oberg Erik Jones Franklin Day 1918 Iron and Steel 1st ed The Industrial Press Saunders William Lawrence 1908 Compressed Air Magazine vol XIII Compressed Air Magazine Company Tschorn Gerhart 1963 Spark Atlas of Steels Cast Iron Pig Iron Ferro Alloys and Metals New York The MacMillan Company External links editSpark test pictures of various materials Retrieved from https en wikipedia org w index php title Spark testing amp oldid 1186194238, wikipedia, wiki, book, books, library,

article

, read, download, free, free download, mp3, video, mp4, 3gp, jpg, jpeg, gif, png, picture, music, song, movie, book, game, games.